ULTEM™ 1000E resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WRGyzp_ULTEM-1000E-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming. US FDA and EU Food Contact compliant, NSF 51 Listing. Effective June, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU1000E. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.25 | % | ASTM D570 |
| Equilibrium, 23°C | 1.3 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3590 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 110 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 60 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 3520 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 165 | MPa | ASTM D790 |
| Poisson's Ratio | 0.36 | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 210 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 201 | °C | ASTM D648 |
| Vicat Softening Temperature | 219 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -20 to 150°C | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -20 to 150°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 138 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.010 - 0.020 | % | |
| Cylinder Zone 1 Temp. | 324 - 349 | °C | |
| Cylinder Zone 2 Temp. | 329 - 357 | °C | |
| Cylinder Zone 3 Temp. | 329 - 357 | °C | |
| Cylinder Zone 4 Temp. | 329 - 357 | °C | |
| Cylinder Zone 5 Temp. | 329 - 357 | °C | |
| Adapter Temperature | 329 - 357 | °C | |
| Die Temperature | 327 - 357 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 24 hrsHead - Zone 6 - Top Temperature: 329 - 357 °CHead - Zone 7 - Bottom Temperature: 329 - 357 °CMelt Temperature (Parison): 321 - 357 °CMold Temperature: 66 - 177 °CScrew Speed: 10 - 70 rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MonoSol® D-8534 XR | MonoSol, LLC | PVOH | MonoSol® |
| Nylene® 4114-33 GL HS | Custom Resins Group | Nylon 66 | Nylene® |
| Fainplast PVC CKL 83/5 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| FHR Polypropylene AP6112-HS | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| KumhoSunny PBT/ABS HAB8750 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |