DOW™ LDPE 410E
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WQxrBd_DOW-LDPE-410E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW LDPE 410E low density polyethylene resin is a high transparency resin, used for composite film and high transparency packaging film processing. The resin does not contain slip agent and opening agent, and can be extruded by a common blown film process. The processing melting temperature is between 170 and 195°C, and the melt temperature of the cast film is between 180 and 240°C. At the time of preparation, this resin has the characteristics of excellent processability and drafting properties, excellent toughness and impact resistance, excellent optical properties, and excellent tensile strength and tear strength. Application field:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.925 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.60 - 0.80 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 50 µm | 190 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm | 200 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 50 µm | 22.0 | MPa | ASTM D882 |
| TD : Break, 50 µm | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 450 | % | ASTM D882 |
| TD : Break, 50 µm | 650 | % | ASTM D882 |
| Dart Drop Impact (50 µm) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 500 | g | ASTM D1922 |
| TD : 50 µm | 400 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | 80 | ASTM D2457 | |
| Haze (50.0 µm) | 6.9 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 195 | °C |
| Extrusion instructions |
|---|
| 放大比 1:2.5 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ ATC-000/000 AS BLACK | PolyOne Corporation | Acetal (POM) Copolymer | Stat-Tech™ |
| Westlake LLDPE LF2010 | Westlake Chemical Corporation | LLDPE | Westlake LLDPE |
| BESTNYL SE50VI01AH | Triesa Plastics | Nylon 66 | BESTNYL |
| DAI-EL™ G-902 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Evolue™ SP2520 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |