HANWHA CLNA-8262
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WPNDWA_HANWHA-CLNA-8262.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hanwha CLNA-8262 is a linear low density polyethylene(LLDPE) produced by the UNIPOL process. It can be used as base resin of silane crosslinked low voltage cable insulation by Monosil, Dry silane and Siloxene process. It offers excellent scorch stability and cure property. It contains controlled amount of antioxidant. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.6 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 10% Igepal, F0) | > 2000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec) | 53 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 17.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | < -10 | % | ASTM D638 |
| Change in Ultimate Elongation in Air (135°C, 168 hr) | < -10 | % | ASTM D638 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | > 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | < 2.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | < 4.0E-4 | ASTM D150 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Elongation 1 | < 90 | % | IEC 60502 |
| Set 2 | < 4.0 | % | IEC 60502 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | silane = 0.8 phr |
| 2 . | silane = 0.8 phr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® NBR DN202 | Zeon Corporation | NBR | Nipol® NBR |
| Eleme HIG07060 | Eleme Petrochemical Company Ltd | HDPE | Eleme |
| KRATON® G7720 GI-N | Kraton Polymers LLC | SEBS | KRATON® |
| Sylvin 8396-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ICORENE® 3560 | ICO Polymers NA, A Division of A. Schulman | LLDPE | ICORENE® |