Sangel® WLE100
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Unigel Plásticos |
| Trademark: | Sangel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WPGgEg_Sangel-WLE100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SAN Resin (Styrene / Acrylonitrile copolymer), great processability, high chemical resistance, good rate stiffness/impact, high gloss and tranparence Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 11 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 66.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ASTM D1525 1 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (0.420 µm) | 84.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Nozzle Temperature | 225 to 245 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ CP0437W10L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| CastForm™ PS | 3D Systems | PS (Specialty) | CastForm™ |
| Globalene® PH5201 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| LEMALLOY® BX528A-3 | Mitsubishi Engineering-Plastics Corp | PPE+Nylon 6 | LEMALLOY® |
| Karina GRAY PVC COMPOUND -E 830-18/ 99-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |