Ateva® 2030
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WP5sYs_Ateva-2030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for compounds and masterbatch applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.941 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 20.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 90 | ||
| Shore D | 32 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 9.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 680 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 36.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 53.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 84.0 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1800 UV | RTP Company | Acrylic (PMMA) | RTP |
| Hyundai EP XLPE XP680/Natural | HYUNDAI EP Co., Ltd. | XLPE | Hyundai EP XLPE |
| Iupilon® GSH2020TR 9005 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LNP™ THERMOCOMP™ OF008A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ THERMOCOMP™ |
| SHINSTRA AMG40TKB (PA66) | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |