PLUSTEK RA304G6
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WOyxfi_PLUSTEK-RA304G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS FIBER REINFORCED, HEAT STABILIZED AND HYDROLYSIS RESISTANT POLYAMIDE 66 FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 to 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.30 to 0.40 | % | |
| -- | 0.30 to 0.40 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 5.6 | % | ASTM D570 |
| Saturation, 23°C | 5.6 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 170 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7800 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 280 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C | 10 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 260 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 90 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.70 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 to 280 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 285 to 310 | °C | |
| Mold Temperature | 65.0 to 110 | °C | |
| Injection Pressure | 70.0 to 125 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 to 85.0 | MPa | |
| Back Pressure | 0.350 to 0.700 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ARC-75A | Biomerics, LLC | TPU-PC | Quadrathane™ |
| SUMILITE® NS3450 | Sumitomo Bakelite Co., Ltd. | PP, Unspecified | SUMILITE® |
| ULTEM™ HU2100 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| ACCUTECH™ CP0436W20L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| PermaStat® 604 | RTP Company | ABS | PermaStat® |