Altuglas® SG-10
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Altuglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WOgZdQ_Altuglas-SG-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Altuglas® SG-10 is a Polymethyl Methacrylate Acrylic product. It is available in Asia Pacific or Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 4.5 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.36 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 37 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 37.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 30 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/2U |
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B |
| CLTE - Flow (-30 to 23°C) | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 3.90 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.040 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 1 | 1.490 | ISO 489 | |
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 225 to 245 | °C | |
| Mold Temperature | 60.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN2620PB | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| Premi-Glas® 2206-15 CR-SX | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| RTP 400 HI TFE 10 | RTP Company | PS (HIPS) | RTP |
| Elastron® D D300.A90.B | Elastron USA, Inc. | SBS | Elastron® D |
| LNP™ THERMOCOMP™ MF004S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |