LNP™ THERMOCOMP™ RB004 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WNyp2m_LNP-THERMOCOMP-RB004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RB004 is a compound based on Nylon 66 containing Glass Beads. Also known as: LNP* THERMOCOMP* Compound RB-1004 Product reorder name: RB004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.29 | g/cm³ | |
| -- | 1.28 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.62 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4100 | MPa | ASTM D638 |
| -- | 3970 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 79.0 | MPa | ISO 527-2/5 |
| Break 2 | 80.0 | MPa | ASTM D638 |
| Break | 75.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 3.8 | % | ISO 527-2/5 |
| Break 3 | 3.7 | % | ASTM D638 |
| Break | 3.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 3870 | MPa | ASTM D790 |
| -- 5 | 3710 | MPa | ISO 178 |
| Flexural Stress | 119 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 28 | J/m | ASTM D256 |
| 23°C 6 | 4.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 230 | J/m | ASTM D4812 |
| 23°C 7 | 17 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 2.70 | J | ASTM D3763 |
| -- | 0.820 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 233 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 219 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 81.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 77.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 51 T 30 | Plastcom | PP, Unspecified | SLOVALEN® |
| Nitrovin™ 801-80A | Vi-Chem Corporation | PVC, Unspecified | Nitrovin™ |
| Dryflex® 420501S | ELASTO | SBS | Dryflex® |
| EnCom F2 PC 1212 | EnCom, Inc. | PC | EnCom |
| DOW™ Electrical & Telecommunications HFDK-4201 NT | The Dow Chemical Company | PE, Unspecified | DOW™ Electrical & Telecommunications |