Kingfa MAC-501DY
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WMYMhw_Kingfa-MAC-501DY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa MAC-501DY is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa MAC-501DY are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 50 | % | ASTM D638 |
| Flexural Modulus 3 | 2240 | MPa | ASTM D790 |
| Flexural Strength 4 | 81.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 460 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 124 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 108 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 28 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 105 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 220 - 235 | °C | |
| Middle Temperature | 220 - 240 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 220 - 240 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Back Pressure | 0.300 - 1.00 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 260°CInjection Speed: 60 to 90% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 801 GB 20 CC | RTP Company | Acetal (POM) Copolymer | RTP |
| Tenac™-C GN455 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| YUPLENE® HX3300H | SK Global Chemical | PP Homopolymer | YUPLENE® |
| NIMA NH PA66UT | Ovation Polymers Inc. | Nylon 66 | NIMA |
| Plaslube® POM HO TL1 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |