MAGNUM™ 3453
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WMCYLu_MAGNUM-3453.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM* 3453 ABS is a general purpose injection moulding resin suitable for a wide range of applications. The product combines a medium to high impact impact performance with good flowability. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183/B |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 220°C/10.0 kg | 15 | g/10 min | |
| 230°C/3.8 kg | 5.0 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2280 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 3.20 mm, Injection Molded) | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 3.20 mm, Injection Molded) | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2300 | MPa | ISO 178 |
| Flexural Stress (3.20 mm, Injection Molded) | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Injection Molded | 10 | kJ/m² | |
| 23°C, Injection Molded | 20 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Injection Molded | 9.0 | kJ/m² | |
| 23°C, Injection Molded | 19 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 1(2.00 mm) | 55 | mm/min | ISO 3795 |
| Flame Rating 2 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Carbon Emission 3 | 25.0 | µg/g | VDA 277 |
| Fogging 4 | 97 | % | ISO 294-4 |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V899 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| PVC Film 06-A0370R-80 NT | Teknor Apex Company | PVC, Flexible | PVC Film |
| ExxonMobil™ LLDPE LL 6202.19 | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| GAPEX® RPP40EV03BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| Sylvin 8784-77 Grey 9453 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |