TAROPRENE® 1 A55 E1N
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROPRENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WKsgL0_TAROPRENE-1-A55-E1N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Elastomer Vulcanized. This TPE-V compound combines the typical performance of a vulcanized elastomer with the easy processing of a thermoplastic compound. Taroprene is totally recyclable and it can be produced in standard grades and in tailor-made grades. Available in natural, black and colored grade. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 3 sec) | 55 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% Strain | 2.00 | MPa | |
| 300% Strain | 3.80 | MPa | |
| Tensile Strength 2(Break) | 4.90 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 450 | % | ASTM D412 |
| Tear Strength | 18.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 70°C, 22 hr | 31 | % | |
| 100°C, 22 hr | 35 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 160 to 225 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| 2 . | Die C |
| 3 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5197-92 Green 3145 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polypropylene PPR 7238 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Iupilon® FPR4500 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LNP™ STAT-KON™ ZX05009 compound | SABIC Innovative Plastics Europe | PPE+PS | LNP™ STAT-KON™ |
| ULTEM™ DT1810EV resin | SABIC Innovative Plastics | PEI | ULTEM™ |