3M™ Dyneon™ Fluoroelastomer FC 2122

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	WKkVt7_3MDyneonFluoroelastomerFC2122.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

3M™ Dyneon™ Fluoroelastomer FC 2122 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FC 2122 has an incorporated bisphenol cure system.

Special Features

Process targets: injection and transfer moulding, extrusion and calendering

Very high elongation

Fast curing

Low viscosity version of 3M™ Dyneon™ Fluoroelastomer FC 2152

Proprietary incorporated cure technology

Excellent mould release

Typical Applications
3M™ Dyneon™ Fluoroelastomer FC 2122 is a universal grade which can be processed using different technologies. It is especially suitable for O-rings and moulded goods.

General Information
Features	Low viscosity Fast curing Good demoulding performance Extended tensile rate
Uses	O-rings
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Extrusion Resin transfer molding Calendering Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	25	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 3 sec)	72		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	3.30	MPa	ASTM D412A
Tensile Strength ²	14.8	MPa	ASTM D412A
Tensile Elongation ³(Break)	350	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	28	%	ASTM D1414
200°C, 70 hr ⁵	27	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
Siveras™ LX70G35	Toray Resin Company	LCP	Siveras™
SuperLite® SL550600-100 (3.5mm)	Azdel, Inc.	PP, Unspecified	SuperLite®
DEXFLEX® 1010E	LyondellBasell Industries	TPO (POE)	DEXFLEX®
D-MEC SCR9100	D-MEC Ltd.	Epoxy	D-MEC
LNP™ STAT-KON™ SE003 compound	SABIC Innovative Plastics	Nylon 12	LNP™ STAT-KON™