LNP™ STAT-KON™ DX05499 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WIuwMV_LNP-STAT-KON-DX05499-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DX05499 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. Also known as: LNP* STAT-KON* Compound DX-7 Product reorder name: DX05499 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.66 | % | ISO 294-4 |
| Flow : 24 hr | 0.64 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.11 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.19 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 67.7 | MPa | ASTM D638 |
| Yield | 64.2 | MPa | ISO 527-2 |
| Break | 60.8 | MPa | ASTM D638 |
| Break | 53.8 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.6 | % | ASTM D638 |
| Yield | 4.3 | % | ISO 527-2 |
| Break | 8.3 | % | ASTM D638 |
| Break | 13 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3230 | MPa | ASTM D790 |
| -- | 3100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 101 | MPa | ASTM D790 |
| -- | 109 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 97 | J/m | ASTM D256 |
| 23°C 2 | 9.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2400 | J/m | ASTM D4812 |
| 23°C 3 | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 25.1 | J | ASTM D3763 |
| -- | 34.2 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 133 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 121 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 122 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+9 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.500 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS R760 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Spartech Polycom PP7215 G41 | Spartech Polycom | PP Copolymer | Spartech |
| Moplen HP652P | PolyMirae | PP Homopolymer | Moplen |
| Arnite® A-X07302 (AV2 390 XT-P) | DSM Engineering Plastics | PET | Arnite® |
| SQUARE® LSG6931-20A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |