TRIBIT® 1500G15K
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Samyang Corporation |
| Trademark: | TRIBIT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WGfuZW_TRIBIT-1500G15K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBIT® 1500G15K is a Polybutylene Terephthalate (PBT) product. It is available in Asia Pacific, Europe, or North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 1.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 83.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 4710 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 225 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.20 | ASTM D150 | |
| Dissipation Factor | 0.020 | ASTM D150 | |
| Arc Resistance | 150 | sec | ASTM D495 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200.5 FR | RTP Company | Nylon 66 | RTP |
| Taitacell EPS 301MM | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Karina WHITE PVC COMPOUND 830-10/2-IS-RG-PO (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifor® 5000/V0-AF-EP NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
| Polifor® C L6 GF/30 NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |