Techsil IS803
| Category: | Silicone , Silicone |
| Manufacturer: | Techsil Limited |
| Trademark: | Techsil |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WDGcdp_Techsil-IS803.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECHSIL IS803 is a ready to use, one part room temperature vulcanising (RTV) elastomer, which cures on exposure to moist air to give a permanently elastic rubber. TECHSIL IS803 has excellent temperature resistance in its cured state. It is recommended for industrial applications where a high modulus sealant with good adhesive properties is required. Key Features
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | BS 903 |
| Molding Shrinkage - Flow | < 0.80 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| IRHD Hardness | 38 | BS 903 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | 5.3 | kN/m |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature 1 | -60 to 300 | °C |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Tack Free Time 2(23°C) | 4.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time 3(23°C, 3.00 mm) | 7.0 | hr | |
| Extrusion Rate | 270 | g/min | |
| Young's Modulus 4 | 0.700 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 5(100% Strain) | 0.940 | MPa | BS 903 |
| Tensile Strength 6(Yield) | 2.30 | MPa | BS 903 |
| Tensile Elongation 7(Break) | 290 | % | BS 903 |
| Tear Strength 8 | 5.50 | kN/m | BS 903 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE | |||
| Flow | 3.1E-4 | cm/cm/°C | |
| Transverse | 9.4E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.6E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.5E-3 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | AFS 1540B |
| 2 . | 65%RH |
| 3 . | 65%RH |
| 4 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 5 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 6 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 7 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 8 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN DM311 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Vistamaxx™ 3980FL | ExxonMobil Chemical | PP Elastomer | Vistamaxx™ |
| Keysor PVC KC1500 | Keysor-Century Corporation | PVC, Unspecified | Keysor PVC |
| Karina GRAY PVC COMPOUND 830-18/5-IS-RG-PO (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Piolen® P X7010 | PiO Kunststoffe GmbH & Co KG | PP Homopolymer | Piolen® P |