Zytel® ST801AW NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WDBnSN_ZytelST801AWNC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Super Toughened, UV Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.4 | -- | % | ISO 294-4 |
| Flow | 1.8 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.2 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 1.9 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1900 | 775 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 49.0 | 35.5 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | 27 | % | ISO 527-2 |
| Flexural Modulus | 1800 | 700 | MPa | ISO 178 |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Elongation - MD (Yield) | 9.5 | -- | % | ISO 527-3 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 21 | -- | kJ/m² | ISO 179/1eA |
| -30°C | 23 | 22 | kJ/m² | ISO 179/1eA |
| 23°C | 83 | 120 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | 240 | -- | kJ/m² | ISO 179/1eU |
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 21 | -- | kJ/m² | ISO 180/1A |
| 23°C | 80 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | No Break | -- | ISO 180/1U | |
| 23°C | No Break | -- | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 155 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 1.4E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.2E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 7.1E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 2.4E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | 26 | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.40 | 6.00 | IEC 60250 | |
| 1 MHz | 3.20 | 3.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.0E-3 | 0.18 | IEC 60250 | |
| 1 MHz | 0.011 | 0.038 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | 26 | -- | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.75 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 290 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 300 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Ejection Temperature | 190 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 100 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILENE® P K10T | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| NOVADURAN® 5010R8M | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Huafon JF-W-AL3030 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| LNP™ STAT-KON™ DD0001I compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Sylvin 2990-70 Clear 8382 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |