Cogegum® GFR/340
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Cogegum® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WCprCG_Cogegum-GFR-340.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cogegum®XLPO-HFFR-crosslinkable halogen-free flame retardant composite silane graft compound by adding catalyst masterbatch (SIOPLAS®Method) for moisture curing. Including polyolefin matrix containing flame retardant system, so that the cable has a self-extinguishing function, does not release halogen acid, toxic and corrosive gases and black smoke. This material meets the requirements of RoHS Directive. meets the following standards:-EN 50363-0 G10; EN50363-5 EI8; EN50363-6 EM10; IEC 60092/351 HF90; Cenelec HD 624.6;VDE 0266 HXI1, HXM1; VDE 0250 HI3; VDE 0207 HJ1, HM1. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.34 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 2(190°C/21.6 kg) | 7.0 | g/10 min | Internal method |
| Water absorption rate- 24 hours (100°C) | mg/cm² | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact test (-40°C) | Pass | IEC 60811 | |
| Thermoset 3 | IEC 60811 | ||
| 250°C, maximum permanent elongation after cooling | 0.0 | % | IEC 60811 |
| 250°C, load elongation at break | 60 | % | IEC 60811 |
| Hot air shrinkage- 1 hour (100°C) | % | IEC 60811 | |
| Hot pressing test- Maximum permeability, K = 0.6 (125°C) | % | IEC 60811 | |
| Bending test (-40°C) | Pass | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation resistance constant | IEC 60502 | ||
| 20°C | 3000 | Mohms·km | IEC 60502 |
| 90°C | 2000 | Mohms·km | IEC 60502 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen-containing acid emission | % | IEC 60754-1 | |
| Latent heat energy- High (Total) | 20.3 | MJ/kg | ISO 1716 |
| Temperature Index (Combustion) | 300 | °C | NES 715 |
| Corrosive gases in flue gas | IEC 60754-2 | ||
| pH | > 4.30 | IEC 60754-2 | |
| Conductivity | µS/mm | IEC 60754-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Ring temperature | 160 - 180 | °C | |
| Head Temperature | 160 - 180 | °C |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Environmental Stress-Cracking Resistance (condition a, 50°C, 3.00mm, 10% Igepal, molding) | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 36 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 13.0 | MPa | IEC 60811 |
| Tensile Elongation (Break) | 290 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| 0.5MPa, change of mechanical properties after air bomb aging test, 127°C, 40 hr | IEC 60811 | ||
| Tensile strength change | 20 | % | IEC 60811 |
| Change in tensile elongation | -10 | % | IEC 60811 |
| Changes in mechanical properties after hot air aging test, 150°C, 240 hr | IEC 60811 | ||
| Tensile strength change | 20 | % | IEC 60811 |
| Change in tensile elongation | -12 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | IEC 60502 | ||
| 20°C | 8.2E+14 | ohms·cm | IEC 60502 |
| 90°C | 5.4E+14 | ohms·cm | IEC 60502 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 31 | % | ASTM D2863 |
| Additional Information |
|---|
| 测试报告采用挤压或挤出样本获得，添加了 3% 的Catalyst CT/2，在95°C热水中交联6小时。着色 EVA 或PE类母粒按重量添加 1.2-1.5%；为了防止加工过程中产生预交联，建议预烘干色母粒( 50-60°C下4-6小时)。 存储 产品必须按下列条件存储： --密封，包装袋完好 环境温度不超过30°C --避免在阳光下曝晒，或露天放置 存放时间过长会造成产品性状改变。 保质期： 9个月 如果没有满足上述条件，苏威特种聚合物不承担任何责任。 包装： 采用防潮袋包装。 每袋25 kg，每只货板堆放1375kg， 每只纸箱750 kg |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 130 - 150 | °C | |
| Cylinder Zone 2 Temp. | 140 - 160 | °C | |
| Cylinder Zone 3 Temp. | 140 - 160 | °C | |
| Cylinder Zone 4 Temp. | 150 - 170 | °C | |
| Die Temperature | 170 - 220 | °C |
| Extrusion instructions |
|---|
| 加工： - -Cogegum® GFR/340 预接枝树脂基体必须加用 CT/2 母粒促进固化。催化剂用量为混合物重量的3％，应在挤塑加工前不超过2-3小时之内进行配混。 最好用挤出机料斗混合。如果需要耐强UV-VIS 辐射、长期抗老化，建议添加5%的CT/7-LR UV催化剂。用原始包装密封存储于干燥环境的催化剂不需要任何预干燥。如需预干燥，可以在50-60℃温度下干燥4-8小时。 -预接枝基体树脂混和物容易受潮，开袋后需在4小时内使用。预接枝基体树脂不可以预先干燥。 挤塑设备： —热塑性塑料标准挤出机，低压缩比（建议压缩比：1：1.2-1.4，L/D：25，恰当调节机筒温度，螺杆较长，需减少催化剂用量。 无需调节螺杆温度 -滤网：无 建议采用压缩装置 固化： -浸入60-70°C温水中 -暴露于环境中，交联时间取决于环境温度和相对湿度 -不管在什么情况下，固化时间都取决于保温厚度，如在温水中强行固化，壁厚 0.7-1.2 mm ，一般需要3~6 小时。 |
| Note Message | |
|---|---|
| 1 . | 23℃ |
| 2 . | The test was performed without adding catalyst MB |
| 3 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9468-65 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Tufpet PBT G2130 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| TRILOY® 120H | Samyang Corporation | PC+PBT | TRILOY® |
| Niplene F15 | Soredi S.p.a. | PP Homopolymer | Niplene |
| Abistir® UG GB/20 NATURALE | SO.F.TER. SPA | ABS | Abistir® |