STERLENE™ KB010-A4001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | R&P (Pte.) Ltd. |
| Trademark: | STERLENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WCDYhg_STERLENE-KB010-A4001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STERLENE™ KB010-A4001 Homopolymer Polypropylene (PP)resins with 20% talc suitable for Automotive applications, such as Under-The-Hood (UTH) and Air-Conditioning (HVAC) parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 32 | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.041 | % | Internal Method |
| Ash Content 2(600°C) | 19 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | 23 | % | |
| Flexural Modulus 3(23°C) | 1900 | MPa | ISO 178 |
| Flexural Stress 4(23°C) | 36.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Complete Break) | 5.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 59.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | 30 min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J-2021GR | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| Radilon® A RV300W 3002 NER 5444 | Radici Plastics | Nylon 66 | Radilon® |
| ELASTOSIL® R plus 4305/50 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| ISOTHANE® G1680A-E | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyether | ISOTHANE® |
| PLUSTEK RA301G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |