INNOPOL® PP CS 1-2120 AP
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WAr6DG_INNOPOL-PP-CS-1-2120-AP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL CS 1-2120 AP is a 20 % talc filled compound based on polypropylene homopolymer.This grade is available in nature and custom coloured form. Recommended application INNOPOL ® CS 1-2120 AP is recommended especially for producing products, where high strength, low warpage, long term heat stability and excellent processability are required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 1.6 | kJ/m² | ISO 179/1eA |
| 23°C | 2.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 0°C | 20 | kJ/m² | ISO 179/1eU |
| 23°C | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 125 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A120 |
| -- | 96.0 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 240 | °C | |
| Middle Temperature | 190 - 240 | °C | |
| Front Temperature | 190 - 240 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 15.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold Pressure: 30 to 100% of injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 605Z | RTP Company | ABS | RTP |
| Sylvin 8983-85 White 1196 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AIE PPO 9010F-S140A | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
| apilon 52® TLE 40 | API SpA | TPU-Polyether | apilon 52® |
| LNP™ THERMOCOMP™ RFB71S compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |