EMPOL® BV 307 FR V2
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | EMAS Plastik San.Tic.AS. |
| Trademark: | EMPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WAbrZn_EMPOL-BV-307-FR-V2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polystyrene V2 flammability |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 to 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 4.0 to 14 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 to 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 to 4000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 20.0 to 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 15 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | > 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 | |
| Glow Wire Ignition Temperature | 750 | °C | VDE 0471/2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO F-3900 | Prime Polymer Co., Ltd. | PP Homopolymer | PRIME TPO |
| RTP ESD C 201H | RTP Company | Nylon 66 | RTP |
| Sumitomo PP AV161 | Sumitomo Chemical Asia | PP Copolymer | Sumitomo PP |
| Hyundai EP PA66 LD430 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Karina BEIGE PVC COMPUOND -E 500D08/201 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |