OmniTech™ HDPE TF20
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniTech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WAOybL_OmniTech-HDPE-TF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Talc Reinforced, High Density Polyethylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 1550 | MPa | ASTM D790 |
| Flexural Strength | 29.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 to 249 | °C | |
| Middle Temperature | 204 to 249 | °C | |
| Front Temperature | 204 to 249 | °C | |
| Nozzle Temperature | 204 to 249 | °C | |
| Processing (Melt) Temp | 204 to 249 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1949A-55NT WHT 1165 | Teknor Apex Company | TPE | Telcar® |
| Sylvin 6212-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Tarnamid® T- 27 M | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| TRANSMARE® 14CT30-0.002 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Dutral® TER 4039 | Versalis S.p.A. | EPDM | Dutral® |