Tritan™ MP150
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tritan™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WA70lM_TritanMP150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eastman Tritan copolyester MP150 is a high flow grade of Eastman Tritan. Eastman Tritan copolyester MP150 has viscosity reductions of 40-50% relative to Eastman Tritan copolyester MP100. It is intended for use in extrusion coating processes or where high melt flow rate is desirable. Other outstanding features include good toughness, hydrolytic stability, and heat and chemical resistance. Eastman Tritan copolyester MP150 may be used in food contact applications with restrictions and is compliant with applicable and select sections of USP 35 <661>, ISO10993, and ISO11607. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1580 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 43.0 | MPa | ASTM D638 |
| Fracture | 52.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 210 | % | ASTM D638 |
| Flexural Modulus | 1580 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 64.0 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 130 | µm | |
| Elastic Modulus - MD (Cast Film) | 979 | MPa | ASTM D882 |
| Tensile Strength - MD (Fracture, Extruded Film) | 56.5 | MPa | ASTM D882 |
| Tensile Elongation - MD (Fracture, Extruded Film) | 220 | % | ASTM D882 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 860 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 | |
| Dart Drop Impact (0.127 mm, Cast Film) | 3.50 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 94.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 81.0 | °C | ASTM D648 |
| Glass Transition Temperature | 110 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total) | 91.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 282 | °C | |
| Mold Temperature | 38 - 66 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene LDPE FE 8004 | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| Bayflex® MP-10000 IMR | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| Hostacom TRC 411N G61309 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Clearflex® H&T DFH 20 | Versalis S.p.A. | LLDPE | Clearflex® H&T |
| Durethan® BKV 30 W1 000000 | LANXESS GmbH | Nylon 6 | Durethan® |