PRE-ELEC® CP 1316
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W9R0u7_PRE-ELEC-CP-1316.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC®CP 1316 is a carbon black filled conductive thermoplastic compound based on polyolefin copolymer. In addition to a low electrical resistivity. PRE-ELEC®CP 1316 has an excellent balance of mechanical properties and is easy to extrude or injection mould. Typical applications include flexible extruded profiles or tubes together with flexible injection moulded parts. PRE-ELEC®CP 1316 may also be diluted with 10-30% of EVA or PE-LD. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.12 | % | ASTM D955 |
| Flow direction | 1.2 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 93 | ISO 868 | |
| Shaw D | 43 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 11.0 | MPa | ASTM D638 |
| 4.00 mm | 11.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 500 | % | ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 1100 | MPa | ASTM D790 |
| 4.00 mm | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -20°C 1 | 40 | kJ/m² | ASTM D256, ISO 179 |
| 23°C 2 | No Break | ISO 179, ASTM D256 | |
| Charpy Unnotched Impact Strength 3 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 2°C | No Break | ISO 179 | |
| 23°C | No Break | ASTM D256 | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Notched Izod Impact 4 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 | |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 5 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 35.0 | °C | ASTM D648B, ISO 75-2/Bf |
| Vicat Softening Temperature | 50.0 | °C | ISO 306/A50, ASTM D1525 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+3 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 60.0 | MPa | |
| Injection Rate | Moderate |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 200°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thick |
| 3 . | 4 mm thick |
| 4 . | 4 mm thick |
| 5 . | 4 mm thick |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergadur™ PBT-GL45 BK018 | PolyOne Corporation | PBT | Bergadur™ |
| Geon™ Vinyl Rigid Extrusion L1361 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| KOPLA PP KPT1020 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |
| Huaxia Shenzhou FKM 246V | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |
| Sylvin 6034-85 Yellow 4208 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |