MarFlex® 7308FK
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | MarFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W8CDSR_MarFlex-7308FK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MarFlex®7308FK is a linear low density polyethylene material,. This product is available in North America or Latin America. The processing method is blow molded film. MarFlex®The main features of 7308FK are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.15 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 290 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 345 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 55.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 34.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 400 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 700 | % | ASTM D882 |
| Dart Drop Test - Blown Film (25.4 µm) | 48.3 | kN/m | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25.4 µm | 115.8 | kN/m | ASTM D1922 |
| TD : 25.4 µm | 251.0 | kN/m | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.4 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 18 | % | ASTM D1003 |
| Additional Information |
|---|
| Blown Film produced on 3.5 in extruder, 30:1 L/D, 8 in Die, 80 mil Die Gap, 2.5:1 BUR, 440°F Melt Temperature. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STARFLEX® P 7027-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | STARFLEX® |
| Chiao Fu PA66/6 MB212LST NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66/6 | Chiao Fu PA66/6 |
| Hostacom BFR | LyondellBasell Industries | PP Copolymer | Hostacom |
| KYOCERA KE-520TD-2 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| Sylvin 9077-90 Grey 9604 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |