TECHNYL® A 218 V30 Black 21NS is a polyamide 66, reinforced with 30% of glass fibre, heat stabilized, for injection moulding.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	heat stabilizer
Features	Heat Stabilized - Inorganic Good liquidity Good demoulding performance
Uses	Application in Automobile Field
Agency Ratings	EC 1907/2006 (REACH) EN 45545 UL QMFZ2
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)
Resin ID (ISO 1043)	PA66-GF30

Physical	Dry	Conditioned	Unit	Test Method
Density	1.36	--	g/cm³	ISO 1183/A
Water Absorption				ISO 62
23°C, 24 hr	0.80	--	%	ISO 62
Equilibrium, 23°C, 50% RH	1.7	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	10000	7500	MPa	ISO 527-2/1A
Tensile Stress (Break, 23°C)	190	135	MPa	ISO 527-2/1A
Tensile Strain (Break, 23°C)	3.0	7.0	%	ISO 527-2
Flexural Modulus
23°C	9000	--	MPa	ASTM D790
23°C	9000	6400	MPa	ISO 178
Flexural Strength
23°C	290	--	MPa	ASTM D790
23°C	280	185	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	11	15	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	75	88	kJ/m²	ISO 179/1eU
Notched Izod Impact
23°C	120	--	J/m	ASTM D256
23°C	10	18	kJ/m²	ISO 180
Unnotched Izod Impact Strength (23°C)	60	65	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	260 260	--	°C	ISO 75-2/Bf
1.8 MPa, not annealed	255	--	°C	ISO 75-2/Af
Melting Temperature	262	--	°C	ISO 11357-3

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	6.0E+15	1.0E+13	ohms	IEC 60093
Volume Resistivity	1.0E+15	1.0E+15	ohms·cm	IEC 60093
Dielectric Strength (2.00 mm)	34	29	kV/mm	IEC 60243-1
Relative Permittivity	3.70	4.00		IEC 60250
Dissipation Factor	0.010	0.11		IEC 60250
Comparative Tracking Index				IEC 60112
Solution a	600	600	V	IEC 60112
Solution B	500	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
1.6 mm	HB	--		UL 94
3.2 mm	HB	--		UL 94
Glow Wire Flammability Index (1.6 mm)	700	--	°C	IEC 60695-2-12
Oxygen Index	23	--	%	ISO 4589-2

Additional Information	Dry	Conditioned	Test Method
European Railways Certifications			EN 45545-2
R22	NC	--	EN 45545-2
R23	NC	--	EN 45545-2

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	270 - 280	°C
Middle Temperature	275 - 285	°C
Front Temperature	280 - 290	°C
Mold Temperature	70 - 100	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	W7GLyE_TECHNYLA218V30BLACK21NS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP VLF 84705	RTP Company	PTT	RTP
Celazole® (T Series) TL-60	PBI Performance Products, Inc.	PBI	Celazole® (T Series)
Europrene® 1778	Versalis S.p.A.	SBR, Emulsion	Europrene®
XENOY™ CL100S resin	SABIC Innovative Plastics Europe	PC+PBT	XENOY™
Hifax TRS 123D NAT	LyondellBasell Industries	TPO (POE)	Hifax