MAJORIS HPS X750
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W6Qfmz_MAJORIS-HPS-X750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS HPS X750 is a greyish, mineral filled high density polyphenylene sulfide compound intended for injection moulding, metallic aspect (only grey colour possible). They combine high mechanical, thermal and electrical properties with excellent chemical and oxidation resistance, lower shrinkage. This product is inherently flame retardant UL 94 V0. APPLICATIONS MAJORIS HPS X750 is intended for the injection moulding of electrical components and automotive applications including electrical and mechanical systems, such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 3.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 2.00 mm | 0.62 | % | |
| Flow : 2.00 mm | 0.54 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 7300 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 23 | kJ/m² | ISO 179/1eU |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 320 to 340 | °C | |
| Mold Temperature | 140 to 160 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ AR9300 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| LIHAN® I706 | Nanjing Lihan Chemical Co., Ltd. | PEI | LIHAN® |
| Karina BLACK PVC COMPOUND 105900-48/ 1-B-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 2990-75 Clear 8392 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRILOY™ D2000I compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |