SABIC® HDPE F04660 (Blown film)
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W6IqGW_SABIC-HDPE-F04660-Blown-film-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE F04660 is a homopolymer film grade with a broad processing window and high stiffness. It has good moisture barrier properties and can be blended with LDPE and LLDPE to improve film strength and rigidity. Typical applications SABIC® HDPE F04660 is typically used for applications where high stiffness is required. It can be used in the middle layer in a coex structure or blended with LDPE and LLDPE to increase stiffness and mechanical properties. It has good water vapor barrier properties required for certain food packaging. Processing conditions SABIC® HDPE F04660 can be extruded at melt temperaures between 190 and 220°C. Film properties Film properties have been measured on 25 µm blown film with a BUR of 4. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.961 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.70 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 46 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Elastic Modulus - MD (25 µm, Blown Film) | 1250 | MPa | ASTM D882 |
| Elastic Modulus - TD (25 µm, Blown Film) | 1700 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 67.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 37.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 490 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 3.0 | % | ASTM D882 |
| Dart Drop Impact 1(25 µm, Blown Film) | < 20 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 10 | g | ASTM D1922 |
| TD : 25 µm, blown film | 800 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 220 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx F662E43 | The Matrixx Group, Inc. | Nylon 66 | Matrixx |
| Axiall PVC 8765 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Fainplast PVC MPH 57 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Sylvin 8260-70FUV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 6185-80 White 190 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |