Sindustris PC GP5009BFH
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W5teoX_Sindustris-PC-GP5009BFH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PC GP5009BFH is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PC GP5009BFH are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 54.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 80 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2400 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 89.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 540 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 123 | °C | ASTM D648 |
| RTI Elec | 85.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 70.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 250 to 265 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 235 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.200 to 0.600 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1499 X 130922 B | RTP Company | PESU | RTP |
| SUMILITE® PVC VSS-F110 | Sumitomo Bakelite Co., Ltd. | PVC, Unspecified | SUMILITE® PVC |
| Vinnolit® E 70 LF | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| HiFill® PA6/6 GF20 HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Sinelec CCB6965/A | Teknor Apex Asia Pacific PTE. LTD. | PS (Specialty) | SINELEC |