SCHULADUR® PCR GF 45
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W4PZvi_SCHULADUR-PCR-GF-45.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 45% glass fibre reinforced PBT/PET blend |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 11.0 | cm³/10min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 160 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 16000 | MPa | ISO 178 |
| Flexural Stress 2 | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 225 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 208 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 214 | °C | ISO 306/A50 |
| -- | 198 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 25 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.60 mm | HB | IEC 60695-11-10, -20 | |
| 3.20 mm | HB | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 700 | °C | IEC 60695-2-12 |
| 3.00 mm | 800 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50mm, through | 825 | °C | IEC 60695-2-13 |
| 3.00mm, through | 800 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA66G33UTL-NC010 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| Thermoset Plastics DC-441 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Asaflex™ 830 | AKelastomers | SBS | Asaflex™ |
| ELASTOSIL® R 805/75 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Sylvin 8200-70UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |