Integra™ PC-5025 R UV 0001
| Category: | PC , Polycarbonate |
| Manufacturer: | PolySource, LLC |
| Trademark: | Integra™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W3HZQo_IntegraPC5025RUV0001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC, 10.5MFI, Mold Release, UV, Clear |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption (Equilibrium, 23°C) | 0.35 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2340 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 61.4 | MPa | ASTM D638 |
| Fracture | 64.8 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 110 | % | ASTM D638 |
| Flexural Modulus 1(50.8mm span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 2(Yield, 50.8 mm Span) | 92.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 800 | J/m | ASTM D3763 |
| Unnotched Izod Impact (23°C) | 3200 | J/m | ASTM D256 |
| Tensile Impact Strength 3 | 546 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.35mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.35mm | 132 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 93°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : -40 to 93°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 271 - 293 | °C | |
| Middle Temperature | 282 - 304 | °C | |
| Front Temperature | 293 - 316 | °C | |
| Nozzle Temperature | 288 - 310 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 71 - 93 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | Type S |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNOGRAN® ESD PSI BLK | Eurocompound Polymers | PS (GPPS) | TECHNOGRAN® |
| Nylene® 826 | Custom Resins Group | Nylon 6 | Nylene® |
| BESTNYL SE30VI01AH | Triesa Plastics | Nylon 66 | BESTNYL |
| apilon 52c® C 301HV | API SpA | TPU-Polyester | apilon 52c® |
| Dynaflex™ G2780-0001 | PolyOne Corporation | TPE | Dynaflex™ |