Estane® AG 9550 TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W2pKqu_Estane-AG-9550-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® AG 9550 is a Polyether based aliphatic polyurethane designed for flat die extrusion into film and sheet products. Features: Very tough, high modulus, high tear and tensile properties that will impart good impact resistance to bullet-resistant glazing applications. Excellent impact and UV resistance. Uses: Designed for the lamination of glass to glass laminates with exposed edges. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% Strain | 12.4 | MPa | |
| 200% Strain | 17.2 | MPa | |
| 300% Strain | 29.6 | MPa | |
| Tensile Strength 2(Break) | 62.1 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 380 | % | ASTM D412 |
| Tear Strength 4 | 77.1 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -35.0 | °C | DSC |
| CLTE - Flow | 7.0E-3 | cm/cm/°C | Internal Method |
| TMA | Internal Method | ||
| Peak | 155 | °C | |
| Range | 90 to 200 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 5 | 1.499 | ASTM D542 | |
| Transmittance 6(1270 µm) | 90.0 | % | ASTM D1003 |
| Haze 7(1270 µm) | 0.30 | % | ASTM D1003 |
| Yellowness Index 8(1.27 mm) | < 1.0 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | Between two pieces of 1/8 inch glass |
| 6 . | Between two pieces of 1/8 inch glass |
| 7 . | Between two pieces of 1/8 inch glass |
| 8 . | Between two pieces of 1/8 inch glass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon X1900-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| Silamid® M30 | Roonamid a.s. | Nylon 6 | Silamid® |
| WPP PE PEH1TF2-Natural | Washington Penn Plastic Co. Inc. | PE, Unspecified | WPP PE |
| CoolPoly® E4507 | Cool Polymers, Inc. | PC | CoolPoly® |
| Karina WHITE PVC COMPOUND 757-10/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |