DINALEN® 20
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | DIOKI d.d. |
| Trademark: | DINALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W0YXmC_DINALEN-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DINALEN® 20 is low density polyethylene containing no additives. It is primarily intended for blow film extrusion while other processing techniques can be used to a lesser extent. DINALEN® 20 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film. DINALEN® 20 is extruded at recommended melt temperature range between 175°C and 200°C. Recommended film thickness: 0.050 mm to 0.200 mm. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 46 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 200 | MPa | ISO 527-2/200 |
| Tensile Stress | ISO 527-2/200 | ||
| Yield, molding | 11.0 | MPa | ISO 527-2/200 |
| Fracture, molding | 18.0 | MPa | ISO 527-2/200 |
| Tensile Strain (Break, Compression Molded) | 750 | % | ISO 527-2/200 |
| Coefficient of Friction (Blown Film) | > 0.40 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 0.050 mm to 0.200 mm | ||
| Tensile Strength | ISO 527-3/500 | ||
| MD : 50 µm, blown film | 25.0 | MPa | ISO 527-3/500 |
| TD : 50 µm, blown film | 19.0 | MPa | ISO 527-3/500 |
| Tensile Elongation | ISO 527-3/500 | ||
| MD : Broken, 50 µm, blown film | 220 | % | ISO 527-3/500 |
| TD : Broken, 50 µm, blown film | 320 | % | ISO 527-3/500 |
| Dart Drop Impact (50 µm, Blown Film) | 260 | g | ISO 7765-1 |
| Trouser Tear Resistance 1 | ISO 6383-1 | ||
| MD : 50 µm, Blown Film | 78.0 | N/mm | ISO 6383-1 |
| TD : 50 µm, Blown Film | 52.0 | N/mm | ISO 6383-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A50 |
| Melting Temperature | 113 | °C | ISO 11357-3 |
| Optical | Nominal Value | ||
|---|---|---|---|
| Gloss | |||
| 20°, 50.0 µm | > 30 | ||
| 60°, 50.0 µm | 60 |
| Additional Information |
|---|
| Film properties taken from |
| Note Message | |
|---|---|
| 1 . | 250 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-1833 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| AKROMID® B3 GF 30 4 RM-M black (3476) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Halar® 3404DA | Solvay Specialty Polymers | ECTFE | Halar® |
| KumhoSunny PC/ABS HAC8230 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| PELPRENE™ P55B | TOYOBO America, Inc. | TPEE | PELPRENE™ |