CYCOLOY™ C3650 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W0A8Cf_CYCOLOYC3650resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according to DIN VDE 0472/815 for cable channels |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 8.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Water Absorption (Saturation, 23°C) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 124 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 113 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2860 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 64.8 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 51.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/5 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.9 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Yield | 4.5 | % | ISO 527-2/50 |
| Fracture 5 | 35 | % | ASTM D638 |
| Fracture | 55 | % | ISO 527-2/5 |
| Fracture | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2690 | MPa | ASTM D790 |
| -- 7 | 2700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | ISO 179/1eA |
| 23°C | 48 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 690 | J/m | ASTM D256 |
| -30°C 10 | 13 | kJ/m² | ISO 180/1A |
| 0°C 11 | 15 | kJ/m² | ISO 180/1A |
| 23°C 12 | 45 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 65.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 100 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 13 | 102 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 88.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 14 | 91.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 110 | °C | ASTM D1525, ISO 306/B120 11 15 |
| -- | 108 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 60°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 35 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 25 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.80 | IEC 60250 | |
| 60 Hz | 2.80 | IEC 60250 | |
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation Factor | |||
| 50 Hz | 6.0E-3 | ASTM D150 | |
| 60 Hz | 6.0E-3 | ASTM D150 | |
| 50 Hz | 4.0E-3 | IEC 60250 | |
| 60 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz | 6.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.49 mm | 5VB | UL 94 | |
| Oxygen Index | 37 | % | ISO 4589-2 |
| Extrusion instructions |
|---|
| Extrusion Blow Molding Parameters: Adapter - Zone 5 Temperature: 227 - 249 °C Barrel - Zone 1 Temperature: 204 - 232 °C Barrel - Zone 2 Temperature: 216 - 243 °C Barrel - Zone 3 Temperature: 216 - 243 °C Barrel - Zone 4 Temperature: 221 - 249 °C Die Temperature: 238 - 249 °C Drying Temperature: 79 - 91 °C Drying Time: 2 - 4 hrs Drying Time (Cumulative): 8 hrs Head - Zone 6 - Top Temperature: 227 - 249 °C Head - Zone 7 - Bottom Temperature: 227 - 249 °C Maximum Moisture Content: 0 - 0.02 % Melt Temperature (Parison): 227 - 249 °C Mold Temperature: 66 - 88 °C Profile Extrusion Parameters: Adapter Temperature: 227 - 271 °C Barrel - Zone 1 Temperature: 204 - 249 °C Barrel - Zone 2 Temperature: 216 - 260 °C Barrel - Zone 3 Temperature: 216 - 260 °C Barrel - Zone 4 Temperature: 227 - 271 °C Calibrator Temperature: 60 - 82 °C Die Temperature: 227 - 271 °C Drying Temperature: 79 - 91 °C Drying Time: 2 - 4 hrs Drying Time (Cumulative): 8 hrs Melt Temperature: 227 - 271 °C Minimum Moisture Content: 0 - 0.02 % |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 120*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Skyrol® SP91 | SKC Inc. | PET | Skyrol® |
| Unichem 9511A-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| ACCUTECH™ NY0730G20L1 | ACLO Compounders Inc. | Nylon 6 | ACCUTECH™ |
| Cellophane™ 335MS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| EPT 3045 | Mitsui Chemicals, Inc. | EPDM | EPT |