Nycal™ 1820R33 Bk-1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Nycal™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VzGttu_Nycal-1820R33-Bk-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nycal™ 1820R33 Bk-1 is a Polyamide 6 (Nylon 6) material filled with 33% glass fiber. It is available in North America for injection molding. Primary attribute of Nycal™ 1820R33 Bk-1: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 162 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8620 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 218 | °C | |
| 1.8 MPa, Unannealed | 204 | °C | |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 to 79.4 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 288 | °C | |
| Mold Temperature | 65.6 to 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PTFE 6CN X | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| VITAMIDE® AR32BK9018 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| KetaSpire® KT-820FP | Solvay Specialty Polymers | PEEK | KetaSpire® |
| Iupilon® EHR3200 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| POLIMAXX HI630 | IRPC Public Company Limited | PS (HIPS) | POLIMAXX |