XYCOMP® Composite 1000-03
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Greene, Tweed & Co. |
| Trademark: | XYCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vz3cbi_XYCOMP-Composite-1000-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Greene, Tweed offers precision plastics components for a variety of demanding, semiconductor applications. These components are made from a full range of high-performance thermoplastic materials, including our Xycomp® composite materials. Xycomp is ideally suited to replace metal or ceramic compounds due to its high strength, low weight, corrosion resistance and dimensional stability. Xycomp materials may also be used in high-pressure and high-temperature (up to 250°C/482°F) applications. The optimal Xycomp material for a specific application is determined by the unique combination of plastic materials, fibers and fiber orientation, as well as manufacturing techniques. Greene, Tweed provides the necessary application evaluation services to assist in choosing the best performance characteristics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | |
| Water Absorption (24 hr) | 1.0E-3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 2070 | MPa | ASTM D3039 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D3039 |
| Flexural Modulus | 124000 | MPa | ASTM D790 |
| Flexural Strength | 2000 | MPa | ASTM D790 |
| Compressive Modulus | 124000 | MPa | ASTM D3410 |
| Compressive Strength | 1360 | MPa | ASTM D3410 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 143 | °C | DSC |
| CLTE - Flow (< 149°C) | 5.4E-7 | cm/cm/°C | Internal Method |
| Service Temperature | < 250 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.2E-5 | ohms·cm | ASTM D257 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon F2538H-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| AMTOPP CH18 | Inteplast Group | PP, Unspecified | AMTOPP |
| Lanufene LLF 182N | Ras Lanuf Oil & Gas Processing Company (RASCO) | LLDPE | Lanufene |
| Axiall PVC 7434 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Sylvin 86049-50 Red 6238 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |