TECAMID™ GF30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger Inc. |
| Trademark: | TECAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vys3nW_TECAMID-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECAMID® 6/6 GF30 is a 30% glass-fiber reinforced nylon 6/6 material whose important properties include high tensile and flexural strength, stiffness, excellent heat deflection temperature, and superior abrasion and wear resistance. While all TECAMID® materials have high mechanical strength and superior resistance to wear and organic chemicals, TECAMID® 6/6 GF30 has more than double the strength and stiffness of unreinforced nylons and a heat deflection temperature which approaches its melting point. TECAMID® 6/6 GF30 has an excellent balance of properties which make it an ideal material for metal replacement in applications such as automotive parts, industrial valves, railway tie insulators, and other industry uses whose design requirements include high strength, toughness, and weight reduction. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.10 | % | ASTM D570 |
| Saturation | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 88 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 89.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 14 | % | ASTM D638 |
| Flexural Modulus | 4700 | MPa | ASTM D790 |
| Flexural Strength | 135 | MPa | ASTM D790 |
| Compressive Modulus | 4100 | MPa | ASTM D695 |
| Compressive Strength | ASTM D695 | ||
| 1% strain | 25.0 | MPa | ASTM D695 |
| 2% strain | 46.0 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 254 | °C | |
| CLTE - Flow | 4.9E-5 | cm/cm/°C | ASTM D696 |
| Maximum Service Temperature | |||
| Intermittent | 170 | °C | |
| Long Term | 110 | °C |
| Additional Information |
|---|
| Data obtained from extruded shapes material. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-HO-HF-30T | Pro Polymers | PP Homopolymer | Pro-Comp™ |
| Retpol® 7856 HS UV2 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| Moplen EP400M | PolyMirae | PP Copolymer | Moplen |
| DENKA POVAL W-100 | Denka Company Limited | PVOH | DENKA POVAL |
| Dynalloy™ OBC8000-T05 | PolyOne Corporation | TPE | Dynalloy™ |