ASTALOY™ PC/ASA KSV
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vuy6H5_ASTALOY-PC-ASA-KSV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ PC/ASA KSV is a non-halogenated, FR alloy of ASA and Polycarbonate which meets the stringent Underwriter's Laboratory UL94 V-0 test whilst offering a superior weathering performance to standard FR-ASA/PC alloys. ASTALOY™ PC/ASA KSV also features high heat resistance and exceptional impact toughness with typical applications including computer monitors and other electrical assemblies. Note: The letters "U", "W" or "UV" indicate UV stabilisation has been added [ ie: ASTALOY™ PC/ASA KSVU ]. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/3.8 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 58.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 180 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2500 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 620 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 60.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 98.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 112 | °C | ASTM D1525 5 |
| CLTE - Flow | 7.1E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 960 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 235 to 270 | °C | |
| Middle Temperature | 245 to 280 | °C | |
| Front Temperature | 255 to 290 | °C | |
| Processing (Melt) Temp | 245 to 290 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU U380PSRU | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Sinvicomp SRP4606 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Formolene® 5143S | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Geon™ 130 Series 136 | Mexichem Specialty Resins, Inc. | PVC Copolymer | Geon™ 130 Series |
| LCA® ABS 2-0011 | UniPlas, Inc. | ABS | LCA® |