Kinta NB4610G
| Category: | AS , Acrylonitrile Styrene Copolymer |
| Manufacturer: | Kinta Technology (Hong Kong) Co., Ltd. |
| Trademark: | Kinta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VuAAoG_KintaNB4610G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kinta NB4610G is an acrylonitrile styrene copolymer (AS) product, which contains a 10% glass fiber reinforced material. It is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.20 - 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 88 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 87.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus 3 | 5100 | MPa | ASTM D790 |
| Flexural Strength 4 | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 4.50 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 102 | °C | ASTM D648 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 35 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75 - 80 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 200 - 205 | °C | |
| Middle Temperature | 205 - 210 | °C | |
| Front Temperature | 200 - 205 | °C | |
| Nozzle Temperature | 210 - 220 | °C | |
| Processing (Melt) Temp | 205 - 210 | °C | |
| Mold Temperature | 80 - 90 | °C | |
| Injection Pressure | 100 - 130 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bio-Flex® F 1137 | FKuR Kunststoff GmbH | PLA | Bio-Flex® |
| AKROMID® B3 GFM 10/20 1 L black (4679) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Boda BDF25IP | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| DELOXEN 2010 | Vamp Tech | PPE+PS | DELOXEN |
| Plaslube® PA6/6 GF13 TL10 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |