Ingeo™ 3052D
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Vt5bR2_Ingeo-3052D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ingeo biopolymer 3052D, a NatureWorks LLC product, is designed for injection molding applications where the requirements are clarity with heat deflection temperatures lower than 120°F (49°C). See table at right for typical properties. The variety of products made with Ingeo 3052D continues to grow rapidly. Applications include cutlery, cups, plates and saucers, and outdoor novelties, and this is just the beginning. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | |
| Relative Viscosity | 3.30 |
| Optical | Nominal Value | ||
|---|---|---|---|
| Clarity | Transparent |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 3550 | MPa | ASTM D790 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 55.0 to 60.0 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 145 to 160 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.025 | % | |
| Hopper Temperature | 21.1 | °C | |
| Rear Temperature | 166 | °C | |
| Middle Temperature | 193 | °C | |
| Front Temperature | 204 | °C | |
| Nozzle Temperature | 204 | °C | |
| Processing (Melt) Temp | 199 | °C | |
| Mold Temperature | 23.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 100 to 175 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS S-211 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Spartech Polycom SCR1-5006 | Spartech Polycom | ABS | Spartech |
| YUPLENE® R390Y | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| Gallonprene® GP100-8001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Kinta NB6615G | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 66 | Kinta |