Iupilon® GPN2030DF
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VrZtLO_Iupilon-GPN2030DF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® GPN2030DF is a Polycarbonate (PC) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® GPN2030DF are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.4 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7.40 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.050 to 0.25 | % | |
| Flow : 3.20 mm | 0.050 to 0.25 | % | |
| Water Absorption (Saturation, 23°C) | 0.090 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 72.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2 |
| Flexural Modulus | 7700 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 23 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 124 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 118 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 2.7E-5 | cm/cm/°C | |
| Transverse | 3.3E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 260 to 290 | °C | |
| Middle Temperature | 270 to 300 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD 282 | RTP Company | Nylon 66 | RTP |
| SOLARENE H645 | Dongbu Hannong Chemical | PS (HIPS) | SOLARENE |
| Cri-Line GP-715-LV | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| HONES® PPS HS-B7-2 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |
| Karina ORANGE PVC COMPOUND 550D32/ 13-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |