PRE-ELEC® PS 1331
| Category: | PS Alloy , Polystyrene Alloy |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VrMkCE_PRE-ELEC-PS-1331.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PS 1331 is a carbon black filled conductive polystyrene compound with elevated chemical resistance. In addition to a low electrical resistivity. PRE-ELEC®PS 1331 has excellent mechanical properties and is easy to extrude. PRE-ELEC®PS 1331 is suitable for sheet applications in which the requirement for chemical resistance exceeds the normal polystyrene. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 200°C/10.0 kg | 60 | g/10 min | ASTM D1238, ISO 1133 |
| 200°C/5.0 kg | 1.8 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 - 0.60 | % | ASTM D955 |
| Flow direction | 0.40 - 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Transverse flow : Yield | 17.0 | MPa | ASTM D638 |
| Flow : Yield | 31.0 | MPa | ASTM D638 |
| Transverse flow : Yield | 39.0 | MPa | ISO 527-2 |
| Flow : Yield | 33.0 | MPa | ISO 527-2 |
| Across Flow | 17.0 | MPa | ASTM D638 |
| Flow | 32.0 | MPa | ASTM D638 |
| -- 1 | 40.0 | MPa | ISO 527-2 |
| 0.400 mm 2 | 31.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Transverse flow : Yield | 8.0 | % | ISO 527-2 |
| Flow : Yield | 5.0 | % | ISO 527-2 |
| Fracture, 0.400mm 3 | 34 | % | ISO 527-2 |
| Fracture, 0.400mm 4 | 66 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 1500 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | |||
| -20°C | 6.3 | kJ/m² | ASTM D256 |
| -20°C | 8.0 | kJ/m² | ISO 179 |
| 23°C | 25 | kJ/m² | ISO 179, ASTM D256 |
| Charpy Unnotched Impact Strength 6 | |||
| -20°C | 67 | kJ/m² | ASTM D256 |
| -20°C | 65 | kJ/m² | ISO 179 |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 6.30 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 18.9 | kJ/m² | ASTM D256 |
| Notched Izod Impact 7 | ISO 180 | ||
| -20°C | 6.0 | kJ/m² | ISO 180 |
| 23°C | 20 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 8 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648B, ISO 75-2/Bf |
| Vicat Softening Temperature | |||
| -- | 97.2 | °C | ASTM D1525 9 |
| -- | 97.0 | °C | ISO 306/A50 |
| Bending test | |||
| -- 10 | > 1.0E+3 | Cycles | |
| -- 11 | > 1.0E+3 | Cycles |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+4 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 200 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Cylinder Zone 5 Temp. | 210 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 210°C |
| Note Message | |
|---|---|
| 1 . | .4 mm Thickness, Across Flow |
| 2 . | Flow |
| 3 . | Across Flow |
| 4 . | Flow |
| 5 . | 4 mm thickness |
| 6 . | 4 mm thickness |
| 7 . | 4 mm thickness |
| 8 . | 4 mm thickness |
| 9 . | 速率 A (50°C/h), 载荷2 (50N) |
| 10 . | Across Flow, ISO 5626 |
| 11 . | Flow, ISO 5626 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trovidur® ESV | Röchling Engineering Plastics SE & Co. KG | PVC, Rigid | Trovidur® |
| Durethan® BC 550 Z DUSXBL 900116 | LANXESS GmbH | Nylon 6 | Durethan® |
| Envir® PA6G33TL-BK0801 | Barnet | Nylon 6 | Envir® |
| Plenco 04504 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |
| OTECH ALLOY OM5130-Boot | OTECH Corporation | TP, Unspecified | OTECH ALLOY |