Leona™ MR001
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Voz89c_Leona-MR001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ MR001 is a Polyamide 66 (Nylon 66) product filled with mineral. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ MR001 include electrical/electronic applications, engineering/industrial parts and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.52 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 1.0 to 1.1 | -- | % | Internal Method |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.5 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.5 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 85 | 60 | ||
| R-Scale | 120 | 108 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5900 | 3400 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Yield, 23°C | -- | 59.0 | MPa | ISO 527-2 |
| Break, 23°C | 93.0 | 58.0 | MPa | ISO 527-2 |
| -- | 98.0 | 67.0 | MPa | ASTM D638 |
| Tensile Strain | ||||
| Yield, 23°C | -- | 14 | % | ISO 527-2 |
| Break | 6.0 | 7.0 | % | ASTM D638 |
| Break, 23°C | 5.5 | 19 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 5600 | 3300 | MPa | ASTM D790 |
| 23°C | 5800 | 3100 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 157 | 98.0 | MPa | ASTM D790 |
| 23°C | 150 | 84.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 22.0 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 62 | 130 | kJ/m² | ISO 179 |
| Notched Izod Impact | 34 | 39 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 240 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 229 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 160 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 118 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 6.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | ||||
| -- | 1.0E+14 | -- | ohms·cm | ASTM D257 |
| 23°C | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 22 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cellophane™ 360MS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| KumhoSunny PET HEG3645 | Shanghai KumhoSunny Plastics Co., Ltd. | PET | KumhoSunny PET |
| Karina IVORY PVC COMPOUND 807D35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom TRC 333N D72645 | LyondellBasell Industries | PP Copolymer | Hostacom |
| OTECH PVC OW127 - Power Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |