SCHULAMID® 612 GF 65 H IS
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VoTT7l_SCHULAMID612GF65HIS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 65% glass fiber reinforced, Polyamide 612 compound, heat stabilized, improved surface |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.74 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 21.0 | -- | cm³/10min | ISO 1133 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 90.0 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 24000 | 20000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 210 | 180 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.5 | 1.6 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(23°C) | 21200 | -- | MPa | ISO 178 |
| Flexural Stress 2(4.0% strain, 23°C) | 330 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 9.5 | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 65 | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/Af |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 240 - 280 | °C | |
| Mold Temperature | 50 - 90 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3405-3 | RTP Company | LCP | RTP |
| Xuchuan XCW-8060SC | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| DINALON® B1X25 V0-7035 | Grupo Repol | Nylon 6 | DINALON® |
| KEBAFORM® C 90.0 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| EPAMOULD 660D30 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |