Zytel® 77G43L NC010
| Category: | Nylon 612 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VnxVh2_Zytel-77G43L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 43% Glass Reinforced Polyamide 612 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 1.7 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.70 | -- | % | |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12500 | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 165 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 11000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 17 | -- | kJ/m² | |
| -30°C | 17 | 13 | kJ/m² | |
| 23°C | 17 | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 85 | 80 | kJ/m² | |
| 23°C | 100 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 15 | -- | kJ/m² | |
| 23°C | 17 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 217 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 203 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 65.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 218 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 2.1E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 1.6E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 7.3E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.4E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.710 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive XP44-11-1 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| Shuman PP 510 | Shuman Plastics, Inc. | PP Homopolymer | Shuman PP |
| Tenite™ Acetate 105E2R30025 Natural, Trsp | Eastman Chemical Company | CA | Tenite™ Acetate |
| Spartech Polycom SCR1-5010 | Spartech Polycom | ABS | Spartech |
| Hypel® PELD50/.924 | Entec Polymers | LDPE | Hypel® |