TAROMID B 280 R3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VmDX7g_TAROMID-B-280-R3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6 elastomer modified, very high impact resistance, no conditioning required. Available: all colours, UV stabilised (L), release agent (W). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/1.0 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.1 to 1.6 | % | |
| Across Flow | 1.1 to 1.6 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.80 | % | ASTM D570, ISO 62 |
| Saturation | 6.0 | % | ASTM D570 |
| Saturation, 23°C | 6.0 | % | ISO 62 |
| Granule Humidity | < 0.10 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 50.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 75 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1800 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Break | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| 23°C 2 | 40 | kJ/m² | ASTM D256 |
| 23°C | 40 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -25°C, 3.20 mm | 480 | J/m | ISO 180, ASTM D256 |
| 23°C, 3.20 mm | 500 | J/m | ISO 180, ASTM D256 |
| 23°C 3 | > 35 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 170 | °C | ISO 306/B50, ASTM D1525 4 |
| Melting Temperature | 218 | °C | ASTM D211, ISO 121 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 18 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm |
| 2 . | Type 1, Edgewise, Notch A |
| 3 . | 4 mm |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 2673B | Teknor Apex Company | TPV | Sarlink® TPV |
| XENOY™ X5230 resin | SABIC Innovative Plastics Europe | PC+PET | XENOY™ |
| Colorite SF 9511SF | Colorite Polymers | PVC, Unspecified | Colorite SF |
| Isoplast® 302EZ TPU | Lubrizol Advanced Materials, Inc. | ETPU | Isoplast® |
| XYLEX™ HX8300HP resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |