Syncure™ System S100FH
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Syncure™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VlaMqe_Syncure-System-S100FH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Syncure™ systems are two part moisture crosslinkable compounds. S100FH is a UL bulletinized, RoHS and flame retardant cable insulation compound. Graft resin component of this system has approximate shelf life of 6 months from the date of production. Please consult PolyOne for its use past 6 months. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Wire Types |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Gel Content 1 | 68 | % | ASTM D2765 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Tensile strength retention (121°C, 1.91mm) 2 | 95 | % | |
| Elongation retention rate (121°C, 1.91mm) 3 | 90 | % |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame test- level | |||
| -- | Pass | UL 1581 | |
| -- | Pass | CSA FT-2 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Catalyst parent mixture- V-0022G RoHS | 17 | % | |
| Transplant-based resin- S-1054A | 83 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 53 | ASTM D2240 | |
| Shaw D, 10 seconds | 47 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 4(Yield) | 19.3 | MPa | ASTM D638 |
| Tensile Elongation 5(Break) | 400 | % | ASTM D638 |
| Deformation Under Load 6(131°C) | 10.0 | % | UL 1581 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| UL Temperature Rating | 90 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 39 | kV/mm | ASTM D149 |
| Dielectric Constant (10 MHz) | 2.31 | ASTM D150 | |
| Dissipation Factor (10 MHz) | 1.2E-3 | ASTM D150 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| 注释：以上情况代表了在30密耳壁的14 AWG上测量得出的典型属性。存放和搬运：包装打开之后应在48小时之内使用，避免自硬化和报废。 |
| Note Message | |
|---|---|
| 1 . | Cross-linked PE, Method B (Non-Arbitration Test) |
| 2 . | 336 hours, UL standard |
| 3 . | 336 hours, UL standard |
| 4 . | Type 4, 510mm/min |
| 5 . | Type 4, 510mm/min |
| 6 . | 500 g, 1 hr. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AGV 40 Natural | Radici Plastics | Nylon 66 | Radilon® |
| WanBlend® WHT-THF9465T2 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| CALP 9800G-6 | Lion Idemitsu Composites Co., Ltd. | PS (GPPS) | CALP |
| Europrene Latice® 5577 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| Lotader® 8200 | Arkema | EEA | Lotader® |