| Akulon®K224-G4U is a polyamide 6 (nylon 6) material, which contains a 23% glass fiber reinforced material. This product is available in North America,. Akulon®The main characteristics of the K224-G4U are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.30 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 1.1 | -- | % | ISO 294-4 |
| Flow direction | 0.70 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7500 | 4400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | 52.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 6.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.5 | 11 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | 55 | kJ/m² | ISO 179/1eU |
| 23°C | 60 | 110 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.710 mm | HB | -- | IEC 60695-11-10, -20 | |
| 1.50 mm | HB | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 255 - 265 | °C | |
| Middle Temperature | 265 - 275 | °C | |
| Front Temperature | 265 - 280 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 250 - 285 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8301-90LG Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Axiall PVC 1702 Clear 7070 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Expandable PS F32B | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Huafon JF-A-AH5025A | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Sumiliteresin® PR-51587 I | SBHPP | Phenolic | Sumiliteresin® |