DENIBLEND A
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Vamp Tech |
| Trademark: | DENIBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VhZpye_DENIBLEND-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC / ABS, not Flame Retardant compound, good mechanical properties, very good impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.70 | % | |
| Across Flow | 0.70 | % | |
| Water Absorption (Saturation) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 40 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 1 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resalloy™ 285 | Resirene, S.A. de C.V. | Styrene Epoxy Copolymer | Resalloy™ |
| SPESIN® KP212G15V0W3 | Kolon Plastics, Inc. | PBT | SPESIN® |
| Adflex KS021P | LyondellBasell Industries | TPO (POE) | Adflex |
| DIC.PPS FZL-4033 | DIC Corporation | PPS | DIC.PPS |
| Latigloss 57 G/40 F2 | LATI S.p.A. | PPA | Latigloss |