SCHULAMID® 66 MK 30 HI H K1357 GRAU 967370
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VhP5x5_SCHULAMID-66-MK-30-HI-H-K1357-GRAU-967370.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% mineral filled PA 66, impact modified, heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 2.00 mm | 1.4 | -- | % | |
| Flow : 2.00 mm | 1.4 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3200 | 1000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 60.0 | 38.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 12 | > 50 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 3200 | -- | MPa | ISO 178 |
| Flexural Stress | 92.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 10 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | -- | kJ/m² | |
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 115 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 240 | -- | °C | ISO 306/A50 |
| -- | 200 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (3.00 mm) | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 725 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 725 | -- | °C | |
| 3.00 mm | 725 | -- | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CALIBRE™ 302V-15 | Trinseo | PC | CALIBRE™ |
| Fainplast PVC RK 320 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| DOMAMID® A1-025-B30-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| Karina WHITE PVC COMPOUND -E TR-550D10/1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS CT273 | AD majoris | PP, Unspecified | MAJORIS |