4TECH® 9S30000
| Category: | Polyphenylene, Unspecified , Polyphenylene |
| Manufacturer: | 4Plas |
| Trademark: | 4TECH® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VhB7ri_4TECH-9S30000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4TECH 9S30000 is a High Flow Unfilled PPO |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Vertical flow direction | 0.60 | % | |
| Flow direction | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2250 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 40.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 30 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Screw Speed | 250 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Aobang TPU-Polyester 65-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| Ultraform® N 2640 Z6 UNC | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Karina STRAW PVC COMPOUND -E 520-38/ 24-B | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KEBATER® PBT B512A | BARLOG plastics GmbH | PBT | KEBATER® |
| LNP™ LUBRICOMP™ RAL22I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |